GRIS

MARENGO*

Producción

propia

Specific weight: 2.730 Kg/m3

Absorption coefficient: 0.08%

Porosity: 0.1%

Frost index: 0%

Resistance to wearing: 20.0 mm

Resistance to bending: 18.2 MPa

Resistance to compression: 148 MPa

Resistance to impact: 25 cm

Microhardness knoop: 1.873 MPa

Anchorages: 2.550 N

NEGRO LAGUNA*

Producción

propia

Specific weight: 2.730 Kg/m3

Absorption coefficient: 0.08%

Porosity: 0.1%

Frost index: 0%

Resistance to wearing: 20.0 mm

Resistance to bending: 18.2 MPa

Resistance to compression: 148 MPa

Resistance to impact: 25 cm

Microhardness knoop: 1.873 MPa

Anchorages: 2.550 N

NEGRO

PERLA*

Producción

propia

Specific weight: 2.730 Kg/m3

Absorption coefficient: 0.08%

Porosity: 0.1%

Frost index: 0%

Resistance to wearing: 20.0 mm

Resistance to bending: 18.2 MPa

Resistance to compression: 148 MPa

Resistance to impact: 25 cm

Microhardness knoop: 1.873 MPa

Anchorages: 2.550 N

MARFIL DORÉ

Specific weight: 2.720 Kg/m3

Coeficiente de absorción: 0.15%

Porosity: 0.1%

Resistance to  wearing: 0.34 mm

Resistance to bending: 19.4 MPa

Resistance to compression: 123 MPa

Resistance to impact: 42 cm

Microhardness knoop: 1.775 MPa

CREMA MARFIL

Specific weight: 2.720 Kg/m3

Absorption coefficient: 0.15%

Porosity: 0.1%

Resistance to  wearing: 0.34 mm

Resistance to bending: 19.4 MPa

Resistance to compression: 123 MPa

Resistance to impact: 42 cm

Microhardness knoop: 1.775 MPa

BLANCO IBIZA

Specific weight: 2.710 Kg/m3

Absorption coefficient: 0,06%

Porosity: 0,65%

Resistance to wearing: 23 mm

Resistance to bending: 10 MPa

Resistance to compression: 74 MPa

Resistance to impact: 35 cm

MARRÓN IMPERIAL

Specific weight: 2.650 Kg/m3

Absorption coefficient: 0,40%

Porosidad: 1,2%

Resistance to  wearing: 0,55 mm

Resistance to bending: 21 MPa

Resistance to compression: 156 MPa

Resistance to impact: 35 cm

Microhardness knoop: 1539 MPa

ROJO ALICANTE

Specific weight: 2.710 Kg/m3

Absorption coefficient: 0,1%

Porosidad: 0,3%

Resistance to  wearing: 2,42 mm

Resistance to bending: 9 MPa

Resistance to compression: 95 MPa

Resistance to impact: 30 cm

Microhardness knoop: 1500 MPa

ROSA LEVANTE

Specific weight: 2.650 Kg/m3

Absorption coefficient: 0.15%

Porosidad: 0.4%

Frost index: 0.1%

Resistance to  wearing: 8.43 mm

Resistance to bending: 12 MPa

Resistance to compression: 124 MPa

Resistance to impact: 23 cm

Microhardness knoop: 1.520 MPa

EMPERADOR

Specific weight: 2.790 Kg/m3

Absorption coefficient: 0,1%

Porosidad: 1,20%

Resistance to  wearing: 0,5 mm

Resistance to bending: 21 MPa

Resistance to compression: 154 MPa

Resistance to impact: 35 cm

BLANCO

NERA*

Producción

propia

Specific weight: 2.730 Kg/m3

Absorption coefficient: 0.08%

Porosity: 0.1%

Frost index: 0%

Resistance to wearing: 20.0 mm

Resistance to bending: 18.2 MPa

Resistance to compression: 148 MPa

Resistance to impact: 25 cm

Microhardness knoop: 1.873 MPa

Anchorages: 2.550 N

CORALO*

Producción

propia

Specific weight: 2.730 Kg/m3

Absorption coefficient: 0.08%

Porosity: 0.1%

Frost index: 0%

Resistance to wearing: 20.0 mm

Resistance to bending: 18.2 MPa

Resistance to compression: 148 MPa

Resistance to impact: 25 cm

Microhardness knoop: 1.873 MPa

Anchorages: 2.550 N

CALIZA CAPRI

Specific weight: 2.460 Kg/m3

Absorption coefficient: 2,9%

Porosity: 9%

Frost index: 0.05%

Resistance to  wearing: 22.0 mm

Resistance to bending: 11,4 MPa

Resistance to compression: 79 MPa

Resistance to impact: 25 cm

Microhardness knoop: 1.569 MPa

Anchorages: 2.000 N

PIEDRA DE BETIES

Specific weight: 2.413 Kg/m3

Absorption coefficient: 3,4%

Porosity: 12,9%

Frost index: 0%

Resistance to  wearing: 2.8 mm

Resistance to bending: 61 MPa

Resistance to compression: 104 MPa

Resistance to impact: 45 cm

Microhardness knoop: 1.273 MPa

Anchorages: 1.741 N

BATEIG AZUL

Specific weight: 2.270 Kg/m3

Absorption coefficient: 4,9 %

Porosity: 18 %

Frost index: 0,01 %

Resistance to  wearing: 21.0 mm

Resistance to bending: 12,7 MPa

Resistance to compression: 84 MPa

Resistance to impact: 25 cm

LUMAQUELA

Specific weight: 2.180 Kg/m3

Absorption coefficient: 6,3 %

Porosity: 10 %

Frost index: 0,16%

Resistance to  wearing: 20.0 mm

Resistance to bending: 7,5 MPa

Resistance to impact: 22 cm

Anchorages: 1.100 N

NIWALA CREMA

Specific weight: 2.206 Kg/m3

Absorption coefficient: 5 %

Porosity: 10%

Frost index: 6%

Resistance to  wearing: 26 mm

Resistance to bending: 6,6 MPa

Resistance to compression: 38 MPa

Resistance to impact: 25 cm

Anchorages: 850 N

CALIZA ALBA

Specific weight: 2.180 Kg/m3

Absorption coefficient: 5,21%

Porosity: 11,7 %

Frost index: 0%

Resistance to  wearing: 31 mm

Resistance to bending: 6,5 MPa

Resistance to compression: 55 MPa

Resistance to impact: 22 cm